STUDI AWAL MATERIAL KOMPOSIT TAHAN PELURU BERPENGUAT SERAT BAMBU DAN KERAMIK MENGGUNAKAN MATRIK RESIN EPOKSI/HARDENER DENGAN VARIASI FRAKSI VOLUME KERAMIK

Abstract

The developments in the manufacture of bulletproof material currently received is very advanced , by making with matrik composite and metallic amplifier until non metal .In this research composite made of natural fibers namely bamboo fiber betung are plaited distance horizontally meetings and the vertical distance is 1.5 cm among plus ceramic fibers using matrik epoxy resin / hardener with variations volume 20 mls ceramics , 25 and 30 mls mls .The test was conducted on composite this is ballistic test bb gun bullet tin with bullet caliber 4.5 mm and heavy 8.3 gr , variations in distance shots for every specimen 2 m , 2.5 m and 3 m. Test was done with composite this is ballistic test bb gun bullets tin with the caliber of bullets 4.5 mm and heavy 8.3 gr, variations in distance shots for every specimens 2 m, 2.5 m and 3 m. the result of this research demonstrating ability material bulletproof who lead to results is the best is materially bulletproof to the volume of ceramic 25 ml and 30 ml can be seen from a picture photo macro 4.4, 4.5, 4.6, 4.7 and 4.8 having a trace the depth of the best namely & lt; 0.03 mm and lowest is the womb volume ceramic 20 ml can be seen at the photos macro graph 4.1, 4.2, and 4.3 where only 0,03mm < depth 0,1mm.