PERBANDINGAN SIFAT MEKANIKAL HASIL PENGELASAN PROSES SMAW (SHIELD METAL ARC WELDING) MENGGUNAKAN ELEKTRODA E6013 DAN E7018 PADA MATERIAL STRUKTUR SESUAI DENGAN STRUCTURAL WELDING CODE AWS D1.1 2010

Abstract

Penelitian ini dilatarbelakangi karena adanya aplikasi struktur konstruksi baja yang
disambung dengan menggunakan las yang tidak berdasarkan standar dan desain pengelasan
yang sesuai dengan Structural Welding Code AWS D1.1 Penelitian ini menggunakan metode
eksperimental. Material JIS B3101 SS400 tebal 10 mm, dengan elektroda E6013 dan elektroda
E7018. Pengujian yang dilakukan meliputi Tensile Test, Charpy V-Notch (CVN), Face Bend dan
Root Bend Test. Hasil pengujian pada elektroda E6013 nilai kuat tarik rata-rata 418.92 MPa,
nilai rata-rata energi patah adalah 87.7 Joule, dan nilai rata-rata Harga Impak 1,092
Joule/mm2. Sedangkan pada elektroda E7018 didapatkan hasil nilai rata-rata kuat tarik 466.61
MPa, nilai rata-rata energi patah 129.46 Joule dan nilai rata-rata harga impak 1,67 Joule/mm2.
Hasil uji face bend dan root bend menunjukkan hasil pengelasan yang mulus tanpa defect.
Kesimpulan dari penelitian ini adalah hasil pengelasan proses SMAW dengan elektroda E7018
berbeda dan lebih kuat serta lebih tangguh dibandingkan hasil pengelasan dengan elektroda
E6013 dan jika digunakan sesuai prosedur yang tepat dapat menghasilkan sound weld.
ABSTRACT
The research is motivated by the application of structural steel construction which are
connected using a weld that is not based on the standard and design of welding in accordance
with Structural Welding Code AWS D1.1. Research uses experimental methods. Material use JIS
B3101 SS400 thickness 10 mm, with electrodes E6013 and E7018 electrodes. Testing was
conducted on the Tensile Test, Charpy V-Notch (CVN), Face and Root Bend Test. The test
results on the E6013 electrode tensile strength values on average 418.92 MPa, the average
value of fracture energy was 87.7 Joule, and the average Impact value 1.092 Joule/mm2. While
the E7018 electrode results obtained average tensile strength 466.61 MPa, the average of
fracture energy 129.46 Joule and the average of impact 1.67 Joule/mm2. The test results face
and root bend shows a smooth-welded without defects. The conclusion of this study is the result
of the welding process SMAW with E7018 electrodes are different and stronger and more
resilient than welded with E6013 electrodes and when used according to proper procedures can
result in sound weld.
Kata kunci : SMAW,E6013,E7018, Structural Welding Code AWS D1.1 2010.